GUIBAO 4808 Silicone Electronic Potting Sealant
Potting Sealant, Electronic Sealant, Solar Panel Sealant
- Potting the junction boxes of solar modules
- Potting the wind turbines, motors, air cooler machines and other large electromechanical equipment for watertight, thermal dissipation and buffer purposes
- Bonding, fixing and thermal conductive potting for electronic components and electric equipment
- UL certified
- Good flowability as supplied , good self-debubbling performance
- Stable and elastic over the temperature -60℃～ 200℃
- Excellent electrical insulation , and fire resistance performance
- Excellent resistance to water ,moisture
- Excellent adhesion to PPO,PET,PVDF and other materials
- Non-corrosive to copper, aluminium, tin ,silver and many other materials
- FV-0 class fire resistance capability
- Excellent thermal conductivity
Colours
GUIBAO 4808 part A is available in white or black fluid, and part B in clear or shallow yellow liquid. It is white or black fluid after mixing.
Packaging
GB4808 is available in kits: Part A in plastic pails (12kg), part B in plastic pails (2kg); or Part A in plastic pails (3kg), part B in plastic cartridges (300ml, 0.5kg).
For more details, please download:
These values are not intended for use in preparing specifications.
| Test Method | Property | Unit | Result | |||
| As supplied | ||||||
| / | Appearance | Part A: white fluid Part B: shallow yellow liquid | ||||
| GB/T 2794 | Viscosity as mixed at 25 ℃ | mPa•s | 2500~5500 | |||
| GB/T 13477 | Density | g/m³ | 1.36~1.42 | |||
| / | Working time | min. | ≤30 | |||
| / | Curing time | h | ≤24 | |||
| Cured after 7 days at 23±2℃，RH 50±5% | ||||||
| GB/T 531.1 | Hardness | Shore A | 35~50 | |||
| GB/T 528 | Tensile strength | MPa | ≥1.0 | |||
| GB/T 1692 | Volume resistivity | Ω·cm | ≥1×10^14 | |||
| GB/T 1695 | Dielectric breakdown strength | kV/mm | ≥18 | |||
| GB/T 1693 | Dielectric constant（1MHz） | ≤3.5 | ||||
| ISO 22007-2 | Thermal conductivity | W/m·K | ≥0.4 | |||
*GB: Chinese National Standard
ASTM: American Society for Testing and Materials
ISO: International Standardization Organization
Complete technical information and literature, adhesion testing and compatibility testing are available from GUIBAO.
Mix part A base to Part B curing agent at a ratio of 6:1 by weight or 4:1 by volume, and then pot the mixture into the parts of substrates where needed, place at room temperature for initial curing for about 2～4 hours before conducting the next procedure. If precipitation occurs in Part A, just stir it well before use, and this does not affect the performance of the sealant.
When using automatic dispensing machine, set at a ratio of 6:1 by weight or 4:1 by volume of part A to Part B for a test first and then put into use.