High Temperature Heat Shrink Marker Sleeve
Request a Quote
High Temperature Heat Shrink Marker Sleeve, PSFR
High-temperature, Heat Shrinkable Identification Sleeves
Model: PSFR
PSFR-M high temperature heat shrink marker sleeve is a type of heat shrink identification sleeves designed for wire and cable identification in applications with high temperature environments or requiring extreme resistance to fuels, lubricants and cleaning solvents. The PSFR-M high temperature heat shrink marker sleeve is printable using thermal transfer printer, and the identification marks are durable and can remain legible even when exposed to abrasion, aggressive cleaning solvents and industrial fluids.
Standard
AMS-DTL-23053/18, SAE-AS 81531, MIL-STD-202F/Method 215J, UL224, RoHS etc.
Features- Material: fabricated from irradiated, thermally stabilized, flame retarded, modified PVDF
- Application: defense, aerospace, mass transit, etc.
- Operating temperature range: -55℃～ 225℃
- Minimum recovery temperature: 135℃
- Maximum storage temperature: 50℃
- Shrink ratio: 2:1
- Color: white, yellow, other colors are available upon request
- Printing: single sided printing or double sided printing
- Supplied format: ladder-style or continuous sleeve
- Recommended printer: thermal transfer printer
- Recommended ribbon: N85 resin ribbon, black, 100mm(width)×300m(length)
Technical Data
| Property | Testing Requirement | WOER Results |
| Tensile strength (MPa) | 24.3 | 31.3 |
| Ultimate Elongation (%) | 200 | 330 |
| Low temperature flexibility 4 hours at -55±1℃ | No cracking | Pass(no cracking) |
| Heat shock 4 hours at 275±3℃ | No cracking, flowing or dripping | Pass(no cracking, legible after 100 rubs)) |
| Dielectric strength (kV/mm) | 15.7 | 43.0 |
| Volume Resistivity (Ω.cm) | 1.0×1012minimum | 9.1×1012 |
| Corrosive effect | No corrosive | Pass |
| Flammability | VW-1 | Pass |
| Heat aging 168 hours at 225±2℃ | No cracking, flowing or dripping | Pass(no cracking, legible after 100 rubs) |
| Print performance | SAE-AS 81531 | Pass(legible after 100 rubs) |
| Strokes | MIL-STD-202F | Pass |
Shrink ratio-2X
| Order Code | As Supplied (mm) | As Supplied (mm) | |||
| ID (D) | Flatten Width (W2) | Double Wall Thickness | ID (d) | Single Wall Thickness | |
| 2.00±0.20 | 3.7±0.3 | 0.48±0.10 | ≤0.79 | 0.45±0.06 | |
| 2.79±0.20 | 5.0±0.3 | 0.48±0.10 | ≤1.18 | 0.49±0.06 | |
| 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.59 | 0.51±0.06 | |
| 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤2.36 | 0.54±0.06 | |
| 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤3.18 | 0.56±0.06 | |
| 10.2±0.32 | 16.7±0.5 | 0.51±0.11 | ≤4.75 | 0.59±0.06 | |
| 13.5±0.36 | 21.8±0.6 | 0.52±0.11 | ≤6.35 | 0.60±0.07 | |
| 20.1±0.40 | 32.2±0.6 | 0.53±0.11 | ≤9.53 | 0.62±0.07 | |
| 26.7±0.45 | 42.5±0.7 | 0.55±0.12 | ≤12.7 | 0.63±0.07 | |
| 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤19.1 | 0.64±0.07 | |
| 53.0±0.56 | 83.9±0.9 | 0.58±0.13 | ≤25.4 | 0.64±0.08 | |
| 79.4±0.56 | 125.3±1.0 | 0.59±0.13 | ≤38.1 | 0.64±0.09 | |
Shrink ratio-3X
| Order Code | As Supplied (mm) | As Supplied (mm) | |||
| ID (D) | Flatten Width (W2) | Double Wall Thickness | ID (d) | Single Wall Thickness | |
| 2.00±0.20 | 3.7±0.3 | 0.47±0.10 | ≤0.53 | 0.52±0.06 | |
| 2.79±0.20 | 5.0±0.3 | 0.47±0.10 | ≤0.79 | 0.57±0.06 | |
| 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.06 | 0.61±0.06 | |
| 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤1.59 | 0.67±0.06 | |
| 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤2.36 | 0.71±0.06 | |
| 10.2±0.32 | 16.7±0.5 | 0.52±0.11 | ≤3.18 | 0.77±0.06 | |
| 13.5±0.36 | 21.8±0.6 | 0.53±0.11 | ≤4.75 | 0.80±0.07 | |
| 20.1±0.40 | 32.2±0.6 | 0.55±0.11 | ≤6.35 | 0.84±0.07 | |
| 26.7±0.45 | 42.5±0.7 | 0.56±0.12 | ≤8.47 | 0.86±0.07 | |
| 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤12.9 | 0.89±0.07 | |
| 53.0±0.56 | 83.9±0.9 | 0.57±0.1 | ≤17.2 | 0.90±0.08 | |
| 79.4±0.56 | 125.3±1.0 | 0.57±0.13 | ≤25.8 | 0.92±0.09 | |