Heat Shrink Wire Marker, Printable Heat Shrink Tubing
Model: CYG-MT
Material: Radiation-crosslinked modified polyolefin
Shrink ratio: 3:1
Application
3:1 printable heat shrink tubing, with a product ID of CYG-MT, is designed to meet the high performance identification requirements for cables and equipment in a variety of manufacturing applications. Because the main material is a radiated cross linked modified polyolefin, it features an excellent abrasion and flame resistance, making it applicable for operation temperature ranges of - 55 ℃ to 135 ℃ for line identification in electrical equipment. The print performance of the material not only meets with SAE-AS-81531.4.6.2 and MIL-STD-202F standards, but is also inflammable and features an outstanding insulation performance. CYG’s 3:1 heat shrink tubing can be double printed and maintains its excellent print performance, even after long term rubbing, or exposure to harsh solvents and oils.
Size (Inch) | As supplied | After recovery | |
Inside diameter (mm) | Inside diameter (mm) | Wall thickness (mm) | |
3/32 | 2.4 | 0.8 | 0.53±0.08 |
1/8 | 3.2 | 1.07 | 0.58±0.08 |
3/16 | 4.8 | 1.6 | 0.58±0.08 |
1/4 | 6.4 | 2.11 | 0.61±0.08 |
3/8 | 9.5 | 3.2 | 0.61±0.08 |
1/2 | 12.7 | 4.2 | 0.61±0.08 |
3/4 | 19.1 | 6.35 | 0.64±0.08 |
1 | 25.4 | 8.46 | 0.64±0.08 |
1-1/2 | 38.1 | 12.7 | 1.0±0.08 |
2 | 50.8 | 16.9 | 1.0±0.08 |
Item | Test methods | Specifications |
Tensile Strength | SAE-AMS-DTL-23053 | ≥10.3MPa |
Ultimate Elongation Ratio | SAE-AMS-DTL-23053 | ≥200% |
Flexibility | SAE-AMS-DTL-23053.4.6.7 | -55℃±1℃, 4h, No cracking |
Heat Shock | SAE-AMS-DTL-23053.4.6.8 | 250℃±3℃, 4h, No cracking, no dripping, no flowing |
Aging Performance | SAE-AMS-DTL-23053.4.6.9 | 175℃±2℃, 168h, No visual damage |
Tensile Strength After Aging | SAE-AMS-DTL-23053.4.6.13 and ASTM D638 | ≥6.9MPa, 23℃±2℃ |
Ultimate Elongation Ratio After Aging | SAE-AMS-DTL-23053.4.6.13 and ASTM D638 | ≥100%, 23℃±2℃ |
Color Stability | SAE-AMS-DTL-23053.4.6.15 | 175℃±2℃, 24h, Pass |
Dielectric Strength | SAE-AMS-DTL-23053.4.6.13 and ASTM D2671 | ≥19.7kV/mm, 23℃±2℃ |
Volume Resistance | SAE-AMS-DTL-23053.4.6.13 and ASTM D876 | ≥1.0x1014Ω· cm,500V(DC), 60s |
Flammability | UL224 | Flame resistance |
Fluid Resistance | AE-AMS-DTL-23053.4.6.11 | No visual damage |
Print Persistence | SAE-AS-81531.4.6.2 | 50 rubber erasure, identification |
Print Solvent Resistance | MIL-STD-202G Method 215K | 10 rubber erasure, identification |
Item | Test methods | Specifications |
Physical performance | ||
Operation temp. | -55℃~135℃ | |
Tensile strength (M Pa) | ASTM D2671 | ≥10.3Mpa |
Ultimate elongation ratio (%) | ASTM D2671 | ≥200% |
Flexibility (-55℃, 4hrs) | ASTM D2671 | No cracking |
Heat shock at 250℃±3℃ at 4hrs | ASTM D2671 | No cracking, no dripping, no flowing |
Electrical performance | ||
Dielectric strength | ASTM D2671 | ≥19.7kV/mm |
Volume Resistance | ASTM D876 | ≥1014Ω·cm |
Flammability | UL224 | Flame resistance |
Fluid resistance (23℃, 24hrs) | ASTM D2671 | Print identified |
After Aging at 175℃±2℃ at 168hrs | ||
Tensile strength (MPa) | ASTM D2671 | ≥6.9Mpa |
Ultimate elongation ratio (%) | ASTM D2671 | ≥100% |
MIL-M-81531-4.6.2 | 20 rubber erasure, identification | |
Print performance | ||
UL 224, | 50 Rubber erasure , identification | |
MIL-M-81531-4.6.2 | 50 Rubber erasure , identification | |
MIL-STD-202 | 30 Rubber erasure, identification |
- The print material meets UL224 and halogen-free environmental standards.
- Print performance meet AS23053/5 requirements.
- Various product packaging methods to meet different customer requirements.
- Can be printed with a standard dot matrix printer or heat transfer printer.
- Readable with double-side printing
- Product color can be customized, with standard colors of white and yellow
- Great anti-pollution ability and print persistence.