GUIBAO 886 Silicone Structural Insulating Glass Sealant

GUIBAO 886 Silicone Structural Insulating Glass Sealant
Request a Quote

structural secondary sealant, secondary seal, silicone sealant, building sealant, IG sealant

Basic Uses
  • GUIBAO 886 Silicone Structural Insulating Glass Sealant is specially designed for use as secondary sealant for structural insulating glass units.
Features
  • Two part, neutral fast cure rate, suitable for factory application
  • High level of tensile strength and mechanical properties
  • Excellent adhesion to a wide range of substrates including coated glass, low -E glass, tempered glass, laminated glass, aluminium and steel spacers etc.
  • Excellent weatherability and high resistance to ultra-violet radiation ,heat and humidity, and ozone
  • Excellent resistance to temperature extremes, unaffected performance from –50 ℃ to 150 ℃
  • Excellent unprimed adhesion to wide range of substrates
  • Good compatibility with other neutral silicone sealants

Colours
Part A (base) of GUIBAO 886 is available in white, part B(curing agent) in black, black colour after mixing.

Packaging
GUIBAO 886 is available in kit: part A base in 200L drums (net 190L), part B is available in 20L pails (net 19L)

For more details, please download:

These values are not intended for use in preparing specifications.

Test Method Property Unit Standard Result
GB/T 13477 (ISO 7390) Slump mm ≤3 0
GB/T 13477 (ISO 9048) Extrusion rate s ≤10 1.9
GB/T 13477 (ASTM D2377) Tack free time h ≤3 1.3
GB/T 13477 (ISO 8339) Modulus at 10% extension MPa ≥0.15 0.22
GB/T 531 (ISO 7619 ) Hardness Shore A 30~60 43
GB/T 13477 (ISO 8340) Adhesion at 25% extension No failure No failure
GB/T 13477 (ISO 8339) Tensile strength at MPa
23℃ ≥0.60 1.13
90℃ ≥0.45 0.87
-30℃ ≥0.45 1.58
water immersion ≥0.45 1.03
water-UV exposure ≥0.45 0.98
GUIBAO 16776 (ASTM C 792) Heat aging
weight loss % ≤6.00 3.4
chalking Nil Nil
cracking Nil Nil

*GB: Chinese National Standard
ASTM: American Society for Testing and Materials
ISO: International Standardization Organization

Complete technical information and literature, adhesion testing and compatibility testing are available from GUIBAO.

Surface Preparation
Clean all joints removing all foreign matter and contaminants such as oil, grease, dust, water, frost, old sealants, surface dirt, or glazing compounds and protective coatings.

Mixing and Dispensing
To obtain the optimal performance of GUIBAO 886, it is recommended that base and curing agent thoroughly mixed using a two-part silicone dispensing machine.
GUIBAO 886 should be mixed at a ratio of 9:1~11:1 base to curing agent by volume, or 11:1~13:1 base to curing agent by weight.
Lot matching of GUIBAO 886 base to curing agent is not required. Before use, it is recommended that curing agent be stirred to ensure the homogeneity of all components.
GUIBAO 886 part B curing agent will react with atmospheric moisture, therefore should not be exposed to air for prolonged period of time.

Priming
Priming is not usually required when using GUIBAO 886.But it is essential that adhesion is tested prior to use to decide whether to use primer or not.

Masking and Tooling
Areas adjacent to joints may be masked to ensure a neat sealant line. Do not allow mask tape to touch clean surfaces to which the silicone sealant is to adhere. Tooling should be completed in one continuous stroke after sealant application. Masking tape should be removed immediately after tooling.

Equipment Cleaning
When not being used, it is recommended that the dispensing equipment be purged either with the base component or flush with suitable solvent.