Carbon Steel Blade, Item CL-30 Doctor Blade
The CL-30 carbon steel blade features superior abrasion resistance compared to the CL-20 doctor blade and uses high quality, German ZAPP 2067 cold rolling carbon steel with overall performance that is 20% better than the base materials of the CL-20. This ensures the CL-30 blade effectively removes greater amounts of ink to ensure a clear printing result.
A heat treatment process has improved the durability and corrosion resistance of the blade, making it suitable for 250m/minute and higher printing press speeds, as well as for use in a variety of other printing presses to remove excess ink.
Parameter2067element content
C | Mn | Si | P | S | Cr |
1.00 | 0.3 | 0.25 | 0.025 | 0.025 | 1.5 |
Tensile strength: 1800-2000 N/mm2
Hardness: 580-600HV
Linearity: 0.15mm/1m
- The hardness levels of the CL-30 blade and CL-20 blade are the same. Blades with a high hardness reduce wear on the cylinder and anilox rollers.
- An improved microstructure gives the blade a better durability and reduces burrs in the blade edge.
- The precise polishing process prevents ink impurities from sticking to the blade surface, thus ensuring a clearer print pattern.
- Compared to CL-20, the blade is more stable in property and its service life can be up to 180000 cylinder rph for black printing.
Size(width) | Maximum speed | Thickness(base material) | Package | |
10mm | 250m/min | 0.152-0.203mm | 100m/box | |
30mm | 250m/min | 0.152-0.203mm | 100m/box | |
40mm | 250m/min | 0.152-0.203mm | 100m/box | |
50mm | 250m/min | 0.152-0.203mm | 100m/box | |
60mm | 250m/min | 0.152-0.203mm | 100m/box |
Note: The above data is standard sizes only. We can customize blade sizes according to customer requirements.
Application
Printing machine: HP, Heidelberg, Koenig&Bauer AG, Komori, Beiren, Manroland, RMGT, etc.
Coating machine: Joinfun, Graco, SATA, Anest Iwata, Hongda, etc.
Rotary printing machine: Dingli, Lisheng, Zhishang, Hengfan, Nashuo, etc.