Aluminum Foil XPE Foam
Aluminum foil XPE foam is a newly developed thermal and acoustic insulation material made from cross-linked polyethylene foam (XPE foam) covered with pure reinforced aluminum foil or aluminum coated film on both sides. The XPE foam as the base material has numerous characteristics of high tensile strength and tear resistance, and it is well suitable for applications requiring insulation materials with properties of thermal insulation, sound proofing, low water absorption, weather durability, chemical resistance and aging resistance. Pure aluminum foil is used as skin laminated to the XPE foam, providing reflective surface, corrosion resistance as well as good heat insulation. Our aluminum foil XPE foams are widely used as reflective insulation material for construction of industrial, commercial and residential building.
Features
- Strong moisture barrier, heat insulation, sound proofing, energy saving
- High tensile strength, superior tear resistance
- Lightweight, flame retardant, easy to cut and install
- Odorless, environmentally friendly
- Low thermal conductivity, excellent thermal insulation
- Keep building warm in winter and cool in summer
- Material: XPE pure aluminum foil (or aluminum coated film)
- Structure: aluminum foil XPE aluminum foil/ aluminum foil IXPE aluminum foil (or customized, e.g. woven fabric aluminum foil)
- Foam density: 30B (33kg/m³)
- Dimensions: 4mm×1350mm×40mts (or customized)
- Thickness: single layer 3-15mm, multi-layer 15-200mm, available in self-adhesive backing on one side
- Flame retardant: UL94 HF-1, GB8624-B1
- Color: grey, black, white
Technical Data
Property | Standard | Unit | Value | |
Density | - | Kg/m3 | 33.33 | |
Tensile strength | Transverse | ISO-1798 | MPa | 0.25~0.27 |
Longitudinal | 0.31~0.32 | |||
Elongation | Transverse | ISO-1798 | % | 137.40~141.20 |
Longitudinal | 159.70-166.00 | |||
Tearing strength | Transverse | ISO-8067 | Kn/m | 1.28~1.33 |
Longitudinal | 1.38~1.40 | |||
Compression 25% | ISO-3386-1 | kPa | 36.40 | |
Compression 40% | ISO-3386-1 | kPa | 62.40 | |
Compression 50% | ISO-3386-1 | kPa | 95.20 | |
Compression set 25% 0.5H | ISO-1856 | % | 19.10 | |
Compression set 25% 24H | ISO-1856 | % | 4.10 | |
Operating temperature range | Internal | ℃ | (-40~ 80) | |
Water absorption % volume(maximum) | Internal | % | 0.50 | |
Thermal conductivity | JISA1412-2 | W/mK | 0.032 | |
Shore- C | ASTM D2240 | ℃ | 22 |