Mixing Blade (for Concrete Mixer)
Name: Mixing blade
Suitable for: Concrete batch plant, concrete mixers of various brands including SANY, ZOOMLION, NFLG, SICOMA, XCMG, Teka, Fangyuan, BHS, Huajian, Shaoguan, JS, etc.
Materials: High manganese steel, modified high manganese steel, alloy steel, bimetal composite material, high chromium material, ultra high chromium cast iron, multi-component alloy steel
Customizable or not: Yes
Part model: Based on customer's needs
Order quantity: Based on customer's needs
Applications
The concrete mixer replacement parts are ideal for the concrete mixers used in cement, chemical, power, metallurgy and other industries.
- Concrete mixer blades for SICOMA mixer
- Concrete mixer blades for SICOMA mixer
- Mixing blades for SANY JS3000 concrete mixer
- Mixing blades for HUAJIAN JS1500b, JS2000b and JS3000b concrete mixers
- Mixing blades for ZOOMLION JS3000 mixer
- JS3000 concrete mixer mixing blades for NFLG HZS180 concrete batch plant
- Mixing blades for BHS2.0, BHS3.0, BHS4.5 and DKXS concrete mixers
- Mixing blades for ELBA1650 and ELBA60 concrete mixers
- Mixing blades for Nikko DSF167, DSF225, DSF275 and DSF330 concrete mixers
- Mixing blades for SHAOGUAN JS3000FG and JS2000FA concrete mixers
Order Information
1. Concrete Mixer Spare Parts
a. Quality standard: National Standard GB/T8263-1999 (Substitute Japanese and ASME products)
b. Supporting concrete mixers: SICOMA, BHS, YKYC, TEKA, SANY, NFLG, FYG, DG; AMMANN, NIKKO, ACP, MARINI; ABG, VOEGELE, DEMAG, DYNAPAC, XCMG
c. Metallographic organization: M M7C3 M23C6
d. Shock toughness: 6-8 J/cm2
| Hardness | 52-62HRC |
| Life | More than 200,000 cubic meter concrete or 300,000 tons asphalt |
| Standards | CN:KM TB Cr 15-25-GTUS:ASTM A532 Class Two Type D |
| Extension strength | 380 N/mm2 |
| Elongation at break | 1% |
| Shock impact (resistance) value | >5 ak N.M/CM2 |
| Flexural strength | >600 ak N.M/CM2 |
| Certifications | ISO9001:2008, |
| Metallographic organization | M M7C3 M23C6 |
| Process | Lost Foam Casting |
| Name | Chemical Compositions % | Hardness | ||||||||
| C | P | S | Si | Mn | Cr | Ni | Mo | Cu | ||
| Special high chrome steel | 2.8~3.1 | <0.06 | <0.06 | 0.8 | 0.8 | 22 | <1 | <1 | <0.5 | 62 |
| High chrome steel | 2.8~3.1 | <0.06 | <0.06 | 0.8 | 0.8 | 15 | <0.5 | 52 | ||
| Low chrome steel | 2.8~3.1 | <0.06 | <0.06 | 0.8 | 0.8 | 3 | 48 | |||
| High manganese steel | 1.2 | <0.06 | <0.06 | 16 | 45 | |||||
| Alloy steel casting | 1.2 | <0.06 | <0.06 | 2 | 1 | 45 | ||||